Abstract：Objective To construct genipin-crosslinked rat acellular spinal cord scaffolds and evaluate their enzymatic degradation rate,biomechanical properties and cytotoxicity.Methods Rat spinal cord scaffolds were decellularized by chemical extraction and chemically crosslinked with 5 g/L genipin solution.Micro-structure of the uncrosslinked and genipin-crosslinked acellular spinal cord scaffolds were observed by HE staining and scanning electron microscopy and properties of pore size,porosity,water ratio,and degradation rate in 2.5 g/L trypsin enzyme solution were examined.Ultimate tensile strength and elastic modulus of normal rat thoracic spinal cord,uncrosslinked and genipin-crosslinked acellular spinal cord scaffolds were determined on Instron mechanical testing instrument.Rat bone marrow mesenchymal stem cells were cultured in lixivium of uncrosslinked and genipin-crosslinked acellular spinal cord scaffolds and MTT assay for relative cell growth rate was test to evaluate the cytotoxicity of scaffolds.Results The uncrosslinked and the genipin-crosslinked acellular spinal cord scaffolds possessed a similar three-dimensional mesh-porous structure with a mean pore diameter about 30 μm and a porosity over 80％,but there was a statistical difference between the two groups(P ＞ 0.05).Water ratio of genipincrosslinked scaffolds was (229.7 ± 12.5) ％,far lower than (283.4 ± 11.2) ％ of uncrosslinked scaffolds (P ＜ O.05) ; genipin-crosslinked acellular spinal cord scaffolds had lower weight loss at each time point than the uncrosslinked acellular spinal cord scaffolds (P ＜ 0.05),but the stability in trypsin,ultimate tensile strength and elastic modulus of acellular spinal cord scaffolds were significantly enhanced by genipin-crosslinking (P ＜ 0.05).Furthermore,no obvious cytotoxicity was observed in the uncroslinked and genipin-crosslinked scaffolds.Conclusions Rat acellular spinal cord scaffolds present no obvious change in structure after genipin-crosslinking,but there is significant improvement in the biomechanical properties and ability against enzymatic degradation and no marked cytotoxicity.Hence,the genipincrosslinked scaffolds are promising in tissue engineering for spinal injury.
. Preparation and biomechanical property of genipin-crosslinked rat acellular spinal cord scaffolds[J]. CHINESE JOURNAL OF TRAUMA, 2014, 30(2): 180-184.